Fabrication and Property of Yb:CaF2 Laser Ceramics from Co-precipitated Nanopowders

Anno: 2019

Autori: Wei JB., Toci G., Pirri A., Patrizi B., Feng YG., Vannini M., Li J.

Affiliazione autori: Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Transparent Optofunct Inorgan Mat, Shanghai 200050, Peoples R China; Univ Chinese Acad Sci, Ctr Mat Sci & Optoelect Engn, Beijing 100049, Peoples R China; CNR, INO, Via Madonna Piano 10C, I-50019 Sesto Fiorentino, Fi, Italy; CNR, IFAC, Via Madonna Piano 10C, I-50019 Sesto Fiorentino, Fi, Italy; CNR, INO, Via G Moruzzi 1, I-56124 Pisa, Pi, Italy

Abstract: Transparent ytterbium doped calcium fluoride ceramics (Yb:CaF2) were successfully fabricated by vacuum sintering and hot pressing post-treatment from coprecipitated powders. In-line transmittance of 5at% Yb:CaF2 transparent ceramics fabricated by pre-sintering at 600 degrees C for 1 h and hot pressing post-treatment at 700 degrees C for 2 h, reaches 92.0% at the wavelength of 1200 nm. Microstructure, spectroscopic characteristics and laser performance of the ceramics were measured and discussed. The sample shows a homogeneous microstructure with average grain size of 360 nm. Furthermore, the absorption cross section at 977 nm and the emission cross section at the 1030 nm of the ceramics are calculated to 0.39×10(-20) cm(2) and 0.26×10(-20) cm(2), respectively. Finally, the laser behavior was tested, finding a maximum output power of 0.9 W while the highest slope efficiency was 23.6%.

Giornale/Rivista: JOURNAL OF INORGANIC MATERIALS

Volume: 34 (12)      Da Pagina: 1341  A: 1348

Maggiori informazioni: National Natural Science Foundation of China (61575212); Key Research Project of the Frontier Science of the Chinese Academy of Sciences (QYZDB-SSW-JSC022)
Parole chiavi: Yb:CaF2; co-precipitation synthesis; two-step sintering; laser ceramics; optical property
DOI: 10.15541/jim20190121

Citazioni: 18
dati da “WEB OF SCIENCE” (of Thomson Reuters) aggiornati al: 2024-04-14
Riferimenti tratti da Isi Web of Knowledge: (solo abbonati)
Link per visualizzare la scheda su IsiWeb: Clicca qui
Link per visualizzare la citazioni su IsiWeb: Clicca qui